PORE STRUCTURE CHARACTERIZATION OF CHEMICALLY MODIFIED BIOCHAR DERIVED FROM RICE STRAW
Autori: Sobhy M. Yakout
Data aparitiei: Februarie / 2014
Revista: Environmental Engineering and Management JournalVol. 14Nr. 2
ISSN: 1843 - 3707
Pret: 25.00 RON    
N.A.

Abstract
Biochar derived from agricultural biomass waste is increasingly recognized as multifunctional material for various applications
according its characteristics. It is therefore essential to investigate biochar properties before large-scale application. In this study,
rice straw-derived biochars produced at different temperature (550, 650, 750 oC). The resulting biochars were subjected to liquidphase
oxidation by different agents including KOH, HNO3, H2SO4, H2O2 and KMnO4 to obtain biochar with different properties.
Pore structure characteristics including surface area, micro and meso pore volume, and pore size distribution were studied.
Biochar surface is sensitive to the type of modifying reagent. Biochars treated by KOH, KMnO4 and H2O2 give higher nitrogen
uptake in the range of micropores and mesopores. The rice straw-derived biochars especially produced at 650oC and treated by
KOH have the highest surface area (179.7 m2/g) and micropore volume (0.081 cc/g) than the rest of biochars. In contrast, biochars
treated by H2SO4 and HNO3 give lower nitrogen uptake and lead to loss of the biochars porosity. Loss of micropore volume is as
low as 10-40% of pore volume in H2SO4 and HNO3 treated biochars. Biochars exhibit wide pore size distribution, from narrow
micropores to wide mesopores. One modal distribution was obtained with peak oscillate in region of 1.0 to 1.3 nm in the case of
micropore region. However, for mesopore region, two minima at about 3.0 nm and 5.0 nm were observed. More homogonous
micropore distribution was produced from KOH and H2O2 treatment in contrast to that of HNO3 and H2SO4 treatment, which give
heterogeneous micropore distribution.



Sus

Acasa · Carti editate · Reviste · Despre editura · Abonament · Contact · Cos cumparaturi · Cum platesc? · Termeni si conditii
VisaMaster CardPayU

2001 - 2024 © Copyright Editura EcoZone Iasi Toate drepturile sunt rezervate.
Gazduire skaleweb.ro

SkaleWeb